S-Plastics Stat-kon OE004AE resin is a compound based on PPS (branched) resin containing carbon fiber. Added feature of this material is Easy
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 163 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 163 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0.8 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 0.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 27160 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 215 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 15710 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 146 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 146 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 19120 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 208 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 16050 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 254 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 47 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 279 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 263 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 262 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.42 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.7 | % | ASTM D 955 |
| Density | 1.42 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 2.E+00 - 4.E+00 | Ohm | ASTM D 257 |
| Source GMD, last updated:03/26/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 315 - 320 | °C |
| Front - Zone 3 Temperature | 330 - 345 | °C |
| Middle - Zone 2 Temperature | 320 - 330 | °C |
| Rear - Zone 1 Temperature | 305 - 315 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/26/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon OE004AE.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|