S-Plastics Stat-kon EXCP0023 resin is PRELIMINARY DATA. 40% carbon fiber reinforced PPS. Conductive: Automotive and business equipment.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 188 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 188 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0.8 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 0.7 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 30890 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 249 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 23710 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 395 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 4 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 267 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.46 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 4.E+00 | Ohm-cm | ASTM D 257 |
| Source GMD, last updated:09/27/2001 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 140 | °C |
| Drying Time | 3 - 4 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 305 - 330 | °C |
| Nozzle Temperature | 305 - 320 | °C |
| Front - Zone 3 Temperature | 315 - 330 | °C |
| Middle - Zone 2 Temperature | 305 - 315 | °C |
| Rear - Zone 1 Temperature | 290 - 305 | °C |
| Mold Temperature | 140 - 160 | °C |
| Back Pressure | 0.3 | MPa |
| Source GMD, last updated:09/27/2001 | ||