S-Plastics Stat-kon EX08308C resin is a high cleanliness Polyimide Compound reinforced with Carbon Fiber for use in applications requiring the highest level of cleanliness. This compound is compounded using LNP CCS Technology.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 188 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 21090 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 209 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 16000 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 309 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 5 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 190 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 4.83E+00 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 4.95E+00 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.387 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.18 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.25 - 0.31 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.36 - 0.42 | % | ASTM D 955 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 2.51E+04 - 2.51E+05 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 4.5E+03 - 9.E+04 | Ohm | ASTM D 257 |
| Static Decay, 5000V to <50V | 0.1 | < seconds | FTMS101B |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.4 | mm | UL 94 |
| Source GMD, last updated:12/31/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 370 - 410 | °C |
| Nozzle Temperature | 350 - 405 | °C |
| Front - Zone 3 Temperature | 360 - 415 | °C |
| Middle - Zone 2 Temperature | 350 - 405 | °C |
| Rear - Zone 1 Temperature | 340 - 395 | °C |
| Hopper Temperature | 80 - 120 | °C |
| Mold Temperature | 140 - 180 | °C |
| Source GMD, last updated:12/31/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon EX08308C.pdf |
|