S-Plastics Stat-kon Noryl_HMC202M resin is DATA ON BK1005 ONLY.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 96 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 96 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4.1 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4.1 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 7580 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 135 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6890 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 86 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 86 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 145 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7150 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 267 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 9 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 180 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 177 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 171 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 181 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 173 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 6.12E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 1.58E-04 | 1/°C | ASTM D 696 |
| CTE, 23°C to 150°C, flow | 1.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.7E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 177 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 50 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.1 - 0.3 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/5.0 kgf | 7.6 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+04 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-1 Flame Class Rating (3) | 1.49 | mm | UL 94 |
| Source GMD, last updated:12/14/2001 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 300 - 325 | °C |
| Nozzle Temperature | 300 - 325 | °C |
| Front - Zone 3 Temperature | 290 - 325 | °C |
| Middle - Zone 2 Temperature | 275 - 320 | °C |
| Rear - Zone 1 Temperature | 265 - 315 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 30 - 70 | % |
| Source GMD, last updated:12/14/2001 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon Noryl_HMC202M.pdf |
|