S-Plastics Stat-kon Noryl_FMC1010 resin is a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL94
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 20 | % | - |
| Tensile Stress, yield, 6.35 mm | 45 | MPa | ASTM D 638 |
| Tensile Strain, break, 6.35 mm | 4.1 | % | ASTM D 638 |
| Flexural Stress, yield, 6.4 mm | 95 | MPa | ASTM D 790 |
| Flexural Modulus, 6.4 mm | 5990 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| FOAM - IMPACT 6.4 mm Wt Reduction | 20 | % | - |
| Izod Impact, unnotched, 23°C, 6.4mm | 154 | J/m | ASTM D 4812 |
| THERMAL | Value | Unit | Standard |
| FOAM - THERMAL 6.4mm Wt Reduction | 20 | % | - |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 103 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 97 | °C | ASTM D 648 |
| Relative Temp Index, Elec | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 50 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 20 | % | - |
| Specific Gravity | 1.15 | - | ASTM D 792 |
| Specific Gravity, foam molded | 0.92 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.15 - 0.25 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.2 - 0.4 | % | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| FOAM - ELECTRICAL 6.4 mm Wt Reduction | 20 | % | - |
| Volume Resistivity | 8.E+03 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.3E+04 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| FOAM - Flame Class Minimum Density | 0.96 | g/cm³ | - |
| UL Recognized, 94V-1 Flame Class Rating (3) | 3.98 | mm | UL 94 |
| Source GMD, last updated:02/08/1993 | |||
| Parameter | ||
| Structural Foam Molding | Value | Unit |
| Blowing Agent, Physical System | Nitrogen Gas | - |
| Blowing Agent, Chemical System | FNC30X | - |
| Concentration Range (Blowing Agent) | 1 - 3 | % |
| Recommended Concentration (Blowing Agent) | 2 | % |
| Drying Temperature (Resin) | 105 - 110 | °C |
| Drying Time (Resin) | 2 - 4 | hrs |
| Drying Time (Resin, Cumulative) | 8 | hrs |
| Melt Temperature | 240 - 280 | °C |
| Nozzle Temperature | 265 - 280 | °C |
| Front Temperature | 260 - 280 | °C |
| Middle Temperature | 250 - 260 | °C |
| Rear Temperature | 240 - 250 | °C |
| Mold Temperature | 65 - 80 | °C |
| Source GMD, last updated:02/08/1993 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon Noryl_FMC1010.pdf |
|