S-Plastics Stat-kon Lexan_EXCP0124 resin is PRELIMINARY DATA. Antistatic, impact modified PC+ABS. Non-ECO flame retardant material.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 54 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 45 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 10 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 56 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 88 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2210 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 459 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 44 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 96 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.26 | - | ASTM D 792 |
| Melt Flow Rate, 260°C/2.16 kgf | 16.2 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 3.E+11 | Ohm | ASTM D 257 |
| Source GMD, last updated:10/19/2001 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 225 - 240 | °C |
| Nozzle Temperature | 220 - 230 | °C |
| Front - Zone 3 Temperature | 220 - 230 | °C |
| Middle - Zone 2 Temperature | 210 - 220 | °C |
| Rear - Zone 1 Temperature | 200 - 210 | °C |
| Mold Temperature | 70 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:10/19/2001 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon Lexan_EXCP0124.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|