S-Plastics Stat-kon DX09301C resin is Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconductor and Hard Disk Drive (HDD) application.Added features of this material include: Clean Compounding System.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 64 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 5.4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 15 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2670 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 101 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 66 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 54 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.1 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 12 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2600 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 99 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2560 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 2160 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 52 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 8 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 200 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 138 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 137 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.224 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.5 - 0.7 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.5 - 0.7 | % | ASTM D 955 |
| Density | 1.22 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+05 - 1.E+08 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+05 - 1.E+08 | Ohm | ASTM D 257 |
| Static Decay, 5000V to <50V | 0.1 | < seconds | FTMS101B |
| Source GMD, last updated:2010/05/21 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2010/05/21 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon DX09301C.pdf |
|