S-Plastics Stat-kon DE0026E resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 117 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 182 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10900 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 1.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 140 | °C | ISO 75/Af |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Source GMD, last updated:09/07/2006 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/07/2006 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon DE0026E.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|