Sabic Stat-kon DD0009XP a compound based on Polycarbonate resin containing Carbon Powder. Added features of this materia

100KG
MOQ
*USD
Price
Sabic Stat-kon DD0009XP a compound based on Polycarbonate resin containing Carbon Powder. Added features of this materia
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 260°C/2.16 Kg: ???
UL Recognized, 94V-0 Flame Class Rating (3): 1.7
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Stat-kon
Certification: COA/ICP Test/Rohs/MSDS
Model Number: DD0009XP
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Stat-kon DD0009XP resin is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material
include:Electrically Conductive, Flame Retardant. Also known as Stat-Kon* D- FR.


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min 54 MPa ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min 1.2 % ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 5.6 % ASTM D 638
Tensile Modulus, 50 mm/min 2820 MPa ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span 108 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2820 MPa ASTM D 790
Tensile Stress, yield, 5 mm/min 62 MPa ISO 527
Tensile Stress, break, 5 mm/min 57 MPa ISO 527
Tensile Strain, yield, 5 mm/min 4.2 % ISO 527
Tensile Strain, break, 5 mm/min 7.5 % ISO 527
Tensile Modulus, 1 mm/min 2810 MPa ISO 527
Flexural Stress, yield, 2 mm/min 102 MPa ISO 178
Flexural Modulus, 2 mm/min 2880 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 1549 J/m ASTM D 4812
Izod Impact, notched, 23°C 69 J/m ASTM D 256
Instrumented Impact Energy @ peak, 23°C 11 J ASTM D 3763
Multiaxial Impact 6 J ISO 6603
Izod Impact, unnotched 80*10*4 +23°C 70 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 6 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT, 0.45 MPa, 3.2 mm, unannealed 141 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 133 °C ASTM D 648
CTE, -40°C to 40°C, flow 3.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 3.2E-05 1/°C ASTM E 831
CTE, 23°C to 60°C, flow 5.36E-05 1/°C ISO 11359-2
CTE, 23°C to 60°C, xflow 5.67E-05 1/°C ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 139 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 131 °C ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.32 g/cm³ ASTM D 792
Moisture Absorption, 50% RH, 24 hrs 0.18 % ASTM D 570
Mold Shrinkage, flow, 24 hrs 0.8 % ASTM D 955
Mold Shrinkage, xflow, 24 hrs 0.7 % ASTM D 955
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+05 - 1.E+10 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3) 1.7 mm UL 94
Source GMD, last updated:2009/01/21    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 305 - 325 °C
Front - Zone 3 Temperature 320 - 330 °C
Middle - Zone 2 Temperature 310 - 320 °C
Rear - Zone 1 Temperature 295 - 305 °C
Mold Temperature 80 - 110 °C
Back Pressure 0.2 - 0.3 MPa
Screw Speed 30 - 60 rpm
Source GMD, last updated:2009/01/21  

 

 


Other related products we recommend:

For more information please download the datesheet

Sabic Stat-kon DD0009XP a compound based on Polycarbonate resin containing Carbon Powder. Added features of this materia 0  Sabic Stat-kon DD0009XP.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 