Sabic Stat-kon DD0001 a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features

100KG
MOQ
*USD
Price
Sabic Stat-kon DD0001 a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 260°C/2.16 Kg: ???
UL Compliant, 94V-0 Flame Class Rating (3)(4): 1.7
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Stat-kon
Certification: COA/ICP Test/Rohs/MSDS
Model Number: DD0001
Payment & Shipping Terms
Packaging Details: 25KG/bag
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Stat-kon DD0001 resin is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of
this material include: Electrically Conductive.


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, break 64 MPa ASTM D 638
Tensile Strain, break 3.6 % ASTM D 638
Tensile Modulus, 50 mm/min 3450 MPa ASTM D 638
Flexural Stress 116 MPa ASTM D 790
Flexural Modulus 3510 MPa ASTM D 790
Tensile Stress, break 64 MPa ISO 527
Tensile Strain, break 3.2 % ISO 527
Tensile Modulus, 1 mm/min 3750 MPa ISO 527
Flexural Stress 103 MPa ISO 178
Flexural Modulus 3520 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 550 J/m ASTM D 4812
Izod Impact, notched, 23°C 23 J/m ASTM D 256
Instrumented Impact Energy @ peak, 23°C 1 J ASTM D 3763
Multiaxial Impact 0 J ISO 6603
Izod Impact, unnotched 80*10*4 +23°C 36 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 2 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT, 0.45 MPa, 3.2 mm, unannealed 86 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 82 °C ASTM D 648
CTE, -40°C to 40°C, flow 5.22E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 5.23E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 5.22E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 5.24E-05 1/°C ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 88 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 82 °C ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.28 g/cm³ ASTM D 792
Moisture Absorption, 50% RH, 24 hrs 0.1 % ASTM D 570
Mold Shrinkage, flow, 24 hrs 0.4 % ASTM D 955
Mold Shrinkage, xflow, 24 hrs 0.4 % ASTM D 955
Mold Shrinkage, flow, 24 hrs 0.39 % ISO 294
Mold Shrinkage, xflow, 24 hrs 0.4 % ISO 294
Moisture Absorption (23°C / 50% RH) 0.14 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+02 - 1.E+06 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant, 94V-0 Flame Class Rating (3)(4) 1.7 mm UL 94 by GE
Source GMD, last updated:09/30/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 80 °C
Drying Time 4 - 6 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 255 - 290 °C
Front - Zone 3 Temperature 260 - 270 °C
Middle - Zone 2 Temperature 255 - 265 °C
Rear - Zone 1 Temperature 250 - 260 °C
Mold Temperature 40 - 65 °C
Back Pressure 0.2 - 0.3 MPa
Screw Speed 30 - 60 rpm
Source GMD, last updated:09/30/2004  

 

 


Other related products we recommend:

For more information please download the datesheet

Sabic Stat-kon DD0001 a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features 0  Sabic Stat-kon DD0001.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Stat-kon DD0001 a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features 1Click to consult and get the latest quotation within 24 hours!