S-Plastics Verton RV007SX9 resin is a compound based on PA 66 resin containing Long Glass Fiber.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 195 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11900 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 283 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 52 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 24 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 263 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 259 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow, 24 hrs | 0.43 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.2 | % | ISO 294 |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 1.3 | % | ISO 62-1 |
| ELECTRICAL | Value | Unit | Standard |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 0.75 | mm | UL 94 |
| Source GMD, last updated:2009/01/08 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 290 - 305 | °C |
| Front - Zone 3 Temperature | 290 - 300 | °C |
| Middle - Zone 2 Temperature | 290 - 300 | °C |
| Rear - Zone 1 Temperature | 280 - 295 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/01/08 |
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton RV007SX9.pdf |
|