S-Plastics Thermocomp DF004XXC resin is Polycarbonate compound, countaining Glass Fiber
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 121 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 188 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 65 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Source GMD, last updated:10/29/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/29/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |