S-Plastics Thermocomp DF004RXP resin is 20% Glass Fiber Reinforced Polycarbonate
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 105 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 102 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 6100 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 173 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 169 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6070 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 103 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5720 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 163 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 163 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 3.7 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 5880 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 895 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 125 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 24 | J | ASTM D 3763 |
| Multiaxial Impact | 5 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 53 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 141 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 2.89E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 5.39E+01 | 1/°C | ASTM D 696 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 140 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.352 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.13 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D 955 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.17 | % | ISO 62-1 |
| Source GMD, last updated:2009/01/27 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/01/27 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp DF004RXP.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|