S-Plastics Thermocomp PCAF04FRHH resin is a 20 % glass reinforced PC+ABS blend without chlorinated or brominated flame retardants. LNP*THERMOCOMP* complies with the material requirements as specified in TCO'99 and Blue Angel ecolabels.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 6200 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 130 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 2.5 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 5800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 23 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 130 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 118 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 8 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 1.5 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 1.5 mm | 825 | °C | IEC 60695-2-13 |
| Source GMD, last updated:04/15/2002 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 230 - 270 | °C |
| Nozzle Temperature | 220 - 260 | °C |
| Front - Zone 3 Temperature | 230 - 270 | °C |
| Middle - Zone 2 Temperature | 220 - 260 | °C |
| Rear - Zone 1 Temperature | 200 - 230 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 50 - 70 | °C |
| Source GMD, last updated:04/15/2002 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp PCAF04FRHH.pdf |
|
Get The Latest Quotation