S-Plastics Thermocomp LF-1006 BK905 resin is a compound based on Polyketone resin containing Glass Fiber.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 175 | MPa | ASTM D 638 |
| Tensile Strain, break | 2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 13230 | MPa | ASTM D 638 |
| Flexural Stress | 241 | MPa | ASTM D 790 |
| Flexural Modulus | 10750 | MPa | ASTM D 790 |
| Tensile Stress, break | 175 | MPa | ISO 527 |
| Tensile Strain, break | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 13100 | MPa | ISO 527 |
| Flexural Stress | 264 | MPa | ISO 178 |
| Flexural Modulus | 12700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 854 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 117 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 14 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 57 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | >298 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | >298 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 4.86E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 1.7E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 4.84E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | >240 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >240 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.54 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.1 | % | ASTM D 570 |
| Density | 1.53 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 0.78 | mm | UL 94 by GE |
| Source GMD, last updated:02/27/2007 | |||