| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 50 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 5.4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 59 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2590 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 84 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2220 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 47 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 5.4 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 47.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 0 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 0 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 547 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 159 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 34 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 144 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 125 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 6.83E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.86E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 6.13E+01 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.89E+01 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 144 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 146 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 172 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.28 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.74 - 0.76 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 36.1 | g/10 min | ASTM D 1238 |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 35 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:12/01/2005 |
Other related products we recommend:
|
For more information please download the datasheet |
|
 |