S-Plastics Thermocomp ZF406XXX resin is a compound based on PPO Blend resin containing Glass Fiber, Flame Retardant. Added features ofthis material include: Flame Retardant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 95 | MPa | ASTM D 638 |
| Tensile Strain, break | 0.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11530 | MPa | ASTM D 638 |
| Flexural Stress | 199 | MPa | ASTM D 790 |
| Flexural Modulus | 11450 | MPa | ASTM D 790 |
| Tensile Stress, break | 119 | MPa | ISO 527 |
| Tensile Strain, break | 1.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11690 | MPa | ISO 527 |
| Flexural Stress | 192 | MPa | ISO 178 |
| Flexural Modulus | 9900 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 523 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 29 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 263 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.98E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 5.76E-05 | 1/°C | ASTM E 831 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 262 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.54 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.7 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.7 | % | ISO 294 |
| Density | 1.53 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.55 | mm | UL 94 by GE |
| Source GMD, last updated:12/17/2004 | |||