S-Plastics Thermocomp ZF0041XC resin is a compound based on PPE+PS Blend resin containing Glass Fiber and Flame retardant. Addedfeatures include Flame Retardant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 80 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6600 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 108 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 117 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 110 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.2 | % | S-Plastics Method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 3 | mm | UL 94 by GE |
| Source GMD, last updated:11/29/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 100 - 120 | °C |
| Drying Time | 2 - 3 | hrs |
| Melt Temperature | 280 - 300 | °C |
| Nozzle Temperature | 260 - 280 | °C |
| Front - Zone 3 Temperature | 280 - 300 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 240 - 260 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 120 | °C |
| Source GMD, last updated:11/29/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp ZF0041XC.pdf |
|