S-Plastics Thermocomp WZ002 resin is a compound based on Polybutylene Terephalate resin containing Milled Glass.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 47 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5000 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2900 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 149 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 64 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 1.9 | % | S-Plastics Method |
| Density | 1.4 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.1 | % | ISO 62-1 |
| Source GMD, last updated:12/31/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 240 - 265 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 245 - 255 | °C |
| Rear - Zone 1 Temperature | 220 - 230 | °C |
| Mold Temperature | 80 - 100 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:12/31/2008 | ||
Other related products we recommend:
For more information please download the datasheet | |
 | S-Plastics Thermocomp WZ002.pdf |