S-Plastics Thermocomp AX06437 resin is a compound based on Acrylonitrile Butadiene Styrene resin containing Mineral.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 37 | MPa | ASTM D 638 |
| Tensile Stress, break | 35 | MPa | ASTM D 638 |
| Tensile Stress, yld, Type I, 5 mm/min | 37 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 34 | MPa | ASTM D 638 |
| Tensile Strain, yield | 1.8 | % | ASTM D 638 |
| Tensile Strain, break | 6 | % | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.8 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 6.9 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3180 | MPa | ASTM D 638 |
| Flexural Stress | 68 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 92 | MPa | ASTM D 790 |
| Flexural Modulus | 3270 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3060 | MPa | ASTM D 790 |
| Tensile Stress, yield | 36 | MPa | ISO 527 |
| Tensile Stress, break | 33 | MPa | ISO 527 |
| Tensile Strain, break | 7.5 | % | ISO 527 |
| Flexural Stress | 64 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 64.1 | % | ISO 178 |
| Flexural Modulus | 3010 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 288 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 26 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*3 +23°C | 3 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 22 | kJ/m² | ISO 180/1U |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 86 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 87 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity, color | 1.17 | - | ASTM D 792 |
| Density | 1.175 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.22 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.5 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 | % | ASTM D 955 |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.32 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Relative Permittivity, 1 GHz | 2.75 | - | ASTM D 150 |
| Dissipation Factor, 1 GHz | 0.0024 | - | ASTM D 150 |
| Source GMD, last updated:01/04/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 - 0.1 | % |
| Melt Temperature | 260 | °C |
| Front - Zone 3 Temperature | 265 - 275 | °C |
| Middle - Zone 2 Temperature | 230 - 245 | °C |
| Rear - Zone 1 Temperature | 205 - 215 | °C |
| Mold Temperature | 70 - 80 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:01/04/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp AX06437.pdf |
|