S-Plastics Thermocomp RF006K resin is a compound based on PA 66 resin containing Glass Fiber. Added features include; Cross Linkable under Beta- or Gamma Radiation.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 175 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.7 | % | ISO 527 |
| Flexural Stress, break, 2 mm/min | 175 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 248 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.1 - 0.3 | % | S-Plastics Method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/26/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/26/2008 | ||