S-Plastics Thermocomp RC006H resin is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include:
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 266 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 27780 | MPa | ASTM D 638 |
| Flexural Stress | 408 | MPa | ASTM D 790 |
| Flexural Modulus | 18750 | MPa | ASTM D 790 |
| Tensile Stress, break | 271 | MPa | ISO 527 |
| Tensile Strain, break | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 22650 | MPa | ISO 527 |
| Flexural Stress | 411 | MPa | ISO 178 |
| Flexural Modulus | 21020 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1014 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 96 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 14 | J | ASTM D 3763 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 68 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 261 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.08E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 4.86E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 1.15E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 4.86E-05 | 1/°C | ISO 11359-2 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.278 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.65 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.08 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.56 | % | ISO 294 |
| Wear Factor Washer | 20 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.46 | - | ASTM D 3702 Modified |
| Static COF | 0.36 | - | ASTM D 3702 Modified |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 1.14 | % | ISO 62 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |