S-Plastics Thermocomp UF006S resin is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this materialinclude: Heat Stabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 196 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 13560 | MPa | ASTM D 638 |
| Flexural Stress | 275 | MPa | ASTM D 790 |
| Flexural Modulus | 10210 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 726 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 258 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.28E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.22E-04 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.43 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.2 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.7 | % | ASTM D 955 |
| Wear Factor Washer | 50 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.48 | - | ASTM D 3702 Modified |
| Static COF | 0.43 | - | ASTM D 3702 Modified |
| Source GMD, last updated:12/17/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 | % |
| Melt Temperature | 315 - 330 | °C |
| Front - Zone 3 Temperature | 325 - 340 | °C |
| Middle - Zone 2 Temperature | 315 - 325 | °C |
| Rear - Zone 1 Temperature | 310 - 320 | °C |
| Mold Temperature | 150 - 170 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:12/17/2004 | ||