S-Plastics Thermocomp UF0069S resin is a compound based on Polyphthalamide resin containing Glass Fiber, Flame Retardant. Added featuresof this material include: Flame Retardant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 181 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 13780 | MPa | ASTM D 638 |
| Flexural Stress | 258 | MPa | ASTM D 790 |
| Flexural Modulus | 12060 | MPa | ASTM D 790 |
| Tensile Stress, break | 166 | MPa | ISO 527 |
| Tensile Strain, break | 1.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12070 | MPa | ISO 527 |
| Flexural Stress | 264 | MPa | ISO 178 |
| Flexural Modulus | 12320 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 550 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 2 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 44 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.655 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.24 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.22 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.59 | % | ISO 294 |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.26 | % | ISO 62 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 | % |
| Melt Temperature | 300 - 310 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 290 - 300 | °C |
| Rear - Zone 1 Temperature | 280 - 295 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp UF0069S.pdf |
|