S-Plastics Thermocomp PK0049 resin is a compound based on PA 6 resin containing Glass Bead, Flame Retardant. Added features include;
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 64 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 103 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 103 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 2.8 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 5200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 5.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.4E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 179 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 102 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 1 | % | S-Plastics Method |
| Density | 1.54 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 1 | % | ISO 62-1 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Source GMD, last updated:11/28/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 255 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 260 | °C |
| Middle - Zone 2 Temperature | 250 - 260 | °C |
| Rear - Zone 1 Temperature | 245 - 255 | °C |
| Mold Temperature | 55 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:11/28/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Thermocomp PK0049.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|