S-Plastics Lexan EXRL0144 resin is Transparent polycarbonate resin with antistatic properties.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 143 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 144 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 138 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 126 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 6 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity, ROA | 5.E+12 | Ohm | IEC 60093 |
| Source GMD, last updated:05/27/2004 | |||
| Parameter | ||
| Profile Extrusion | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Melt Temperature | 270 - 280 | °C |
| Barrel - Zone 1 Temperature | 260 - 280 | °C |
| Barrel - Zone 2 Temperature | 260 - 280 | °C |
| Barrel - Zone 3 Temperature | 260 - 280 | °C |
| Barrel - Zone 4 Temperature | 260 - 280 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Adapter Temperature | 260 - 280 | °C |
| Die Temperature | 250 - 260 | °C |
| Calibrator Temperature | 70 - 90 | °C |
| Source GMD, last updated:05/27/2004 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan EXRL0144.pdf |
|