S-Plastics Lexan EXRL0038 resin is a high heat resistant poly(ester)carbonate injection moulding resin.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 85 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2150 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| Hardness, H358/30 | 95 | MPa | ISO 2039-1 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 151 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 153 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 143 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 131 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 13 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:11/13/2002 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Melt Temperature | 300 - 330 | °C |
| Mold Temperature | 100 - 120 | °C |
| Source GMD, last updated:11/13/2002 | ||
|
For more information please download the datesheet |
|
 |