Sabic Lexan OQ3220 resin is Medium-high flow. UV-stabilized. For ophthalmic lenses. In natural and selected colors.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 68 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 125 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
| Purity, particles per gram > 50 microns | 1 | - | SABIC Method |
| Purity, particles per gram 20-50 microns | 40 | - | SABIC Method |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 694 | J/m | ASTM D 256 |
| Tensile Impact, Type "S" | 472 | kJ/m² | ASTM D 1822 |
| Instrumented Impact Energy @ peak, 23°C | 62 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 129 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC Method |
| Melt Flow Rate, 300°C/1.2 kgf | 18 | g/10 min | ASTM D 1238 |
| OPTICAL | Value | Unit | Standard |
| Light Transmission | 89 | % | ASTM D 1003 |
| Haze | 0.6 | % | ASTM D 1003 |
| Refractive Index | 1.586 | - | ASTM D 542 |
| Source GMD, last updated:01/04/2000 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 280 - 305 | °C |
| Nozzle Temperature | 275 - 300 | °C |
| Front - Zone 3 Temperature | 280 - 305 | °C |
| Middle - Zone 2 Temperature | 270 - 295 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Mold Temperature | 70 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:01/04/2000 | ||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | ||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | ||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | ||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | ||
| (4) Internal measurements according to UL standards. | ||
|
For more information please download the datesheet |
|
 |
Sabic Lexan OQ3220.pdf |
|