Sabic Lexan OQ3120 High Flow. UV-Stabilized. Inherent Mold Release. Ophthalmic Lenses.

100KG
MOQ
*USD
Price
Sabic Lexan OQ3120 High Flow. UV-Stabilized. Inherent Mold Release. Ophthalmic Lenses.
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 25
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: OQ3120
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan OQ3120 resin is High Flow. UV-stabilized. Inherent mold release. Ophthalmic lenses.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 65 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 93 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2300 MPa ASTM D 790
Purity, particles per gram > 50 microns 1 - SABIC Method
Purity, particles per gram 20-50 microns 40 - SABIC Method
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 640 J/m ASTM D 256
Instrumented Impact Energy @ peak, 23°C 54 J ASTM D 3763
THERMAL Value Unit Standard
HDT, 1.82 MPa, 6.4 mm, unannealed 126 °C ASTM D 648
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 25 g/10 min ASTM D 1238
OPTICAL Value Unit Standard
Light Transmission 89 % ASTM D 1003
Refractive Index 1.586 - ASTM D 542
Source GMD, last updated:01/04/2000    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 270 - 295 °C
Nozzle Temperature 265 - 290 °C
Front - Zone 3 Temperature 270 - 295 °C
Middle - Zone 2 Temperature 260 - 280 °C
Rear - Zone 1 Temperature 250 - 270 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:01/04/2000  
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION    
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
   
(2) Only typical data for selection purposes. Not to be used for part or tool design.    
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.    
(4) Internal measurements according to UL standards.    

 

 


 

For more information please download the datesheet

Sabic Lexan OQ3120 High Flow. UV-Stabilized. Inherent Mold Release. Ophthalmic Lenses. 0  Sabic Lexan OQ3120.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan OQ3120 High Flow. UV-Stabilized. Inherent Mold Release. Ophthalmic Lenses. 1Click to consult and get the latest quotation within 24 hours!

 