S-Plastics Lexan RL7603resin is Will be commercialized as FXD153. Can be HB UL rated. PRELIMINARY DATA. Transparent/transluscent PC for light diffusion special effects. MFR of 2.5. Extrusion/blowmolding applications.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 65 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 747 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 157 | °C | ASTM D 1525 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 2.5 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:02/17/2000 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 115 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Minimum Moisture Content | 0.01 | % |
| Melt Temperature (Parison) | 265 - 275 | °C |
| Barrel - Zone 1 Temperature | 260 - 275 | °C |
| Barrel - Zone 2 Temperature | 260 - 275 | °C |
| Barrel - Zone 3 Temperature | 260 - 275 | °C |
| Barrel - Zone 4 Temperature | 260 - 275 | °C |
| Adapter - Zone 5 Temperature | 260 - 275 | °C |
| Head - Zone 6 - Top Temperature | 260 - 275 | °C |
| Head - Zone 7 - Bottom Temperature | 260 - 275 | °C |
| Screw Speed | 15 - 50 | rpm |
| Mold Temperature | 65 - 95 | °C |
| Die Temperature | 270 - 280 | °C |
| Source GMD, last updated:02/17/2000 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan RL7603.pdf |
|