S-Plastics Lexan RL3763 resin is a medium viscosity, impact modified grade which is food compliant.
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 65 | MPa | ISO 527 |
Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2250 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 82 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2150 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 12 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 73 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 14 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PHYSICAL | Value | Unit | Standard |
Density | 1.2 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm³/10 min | ISO 1133 |
Source GMD, last updated:08/30/1994 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 2 - 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 280 - 310 | °C |
Nozzle Temperature | 270 - 290 | °C |
Front - Zone 3 Temperature | 280 - 310 | °C |
Middle - Zone 2 Temperature | 270 - 290 | °C |
Rear - Zone 1 Temperature | 260 - 280 | °C |
Hopper Temperature | 60 - 80 | °C |
Mold Temperature | 80 - 110 | °C |
Source GMD, last updated:08/30/1994 |
For more information please download the datesheet | |
![]() | S-Plastics Lexan RL3763.pdf |