S-Plastic Lexan ML9735 Film Extrusion Grade; 6.3 MFR, Non-UV Stabilized PC Resin.

100KG
MOQ
*USD
Price
S-Plastic Lexan ML9735 Film Extrusion Grade; 6.3 MFR, Non-UV Stabilized PC Resin.
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 6.3
Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: ML9735
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Lexan  ML9735 resin is Film extrusion grade; 6.3 MFR, non-UV stabilized PC resin.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 69 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 135 % ASTM D 638
Tensile Modulus, 50 mm/min 2380 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 98 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 70 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 120 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 908 J/m ASTM D 256
Izod Impact, notched 80*10*4 +23°C 65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C 10 kJ/m² ISO 180/1A
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 124 °C ASTM D 648
CTE, -40°C to 95°C, flow 6.8E-05 1/°C ASTM E 831
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 144 °C ISO 306
Vicat Softening Temp, Rate B/120 150 °C ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 127 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % S-Plastics Method
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 300°C/1.2 kgf 6.3 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 6 cm³/10 min ISO 1133
Source GMD, last updated:04/05/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 310 - 330 °C
Nozzle Temperature 305 - 325 °C
Front - Zone 3 Temperature 310 - 330 °C
Middle - Zone 2 Temperature 300 - 320 °C
Rear - Zone 1 Temperature 290 - 310 °C
Mold Temperature 80 - 115 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:04/05/2004  
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.    
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION  
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.    
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.  
(4) Internal measurements according to UL standards.    

 

 


 

For more information please download the datasheet

S-Plastic Lexan ML9735 Film Extrusion Grade; 6.3 MFR, Non-UV Stabilized PC Resin. 0  S-Plastics Lexan ML9735.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic Lexan ML9735 Film Extrusion Grade; 6.3 MFR, Non-UV Stabilized PC Resin. 1Click to consult and get the latest quotation within 24 hours!

 

S-Plastics lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)