Features
Specifications
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: ML7690
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  ML7690 resin is a high viscosity multi purpose U.V. stabilized grade and contains a release agent to ensure easy processing. LEXAN
 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 70 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 120 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 12 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 75 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 15 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
CTE, -40°C to 40°C, xflow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, approximate maximum 140 °C IEC 60695-10-2
Vicat Softening Temp, Rate B/50 144 °C ISO 306
Vicat Softening Temp, Rate B/120 145 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 138 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 127 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Mold Shrinkage on Tensile Bar, flow (2) (5) 0.5 - 0.7 % SABIC Method
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 6 cm³/10 min ISO 1133
Source GMD, last updated:2009/07/20    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 290 - 320 °C
Nozzle Temperature 280 - 310 °C
Front - Zone 3 Temperature 290 - 320 °C
Middle - Zone 2 Temperature 280 - 310 °C
Rear - Zone 1 Temperature 270 - 300 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 80 - 120 °C
Source GMD, last updated:2009/07/20  
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.    
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION    
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.    
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.  
(4) Internal measurements according to UL standards.    
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing
conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or
legacy tooling prior to cutting tools for new molded article.

 
 


 

For more information please download the datasheet

Sabic Lexan ML7690 Is A High Viscosity Multi Purpose U.V. Stabilized Grade And Contains A Release Agent To Ensure Easy 0  Sabic Lexan ML7690.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan ML7690 Is A High Viscosity Multi Purpose U.V. Stabilized Grade And Contains A Release Agent To Ensure Easy 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)