Sabic Lexan HP6NR Resin Is Low/Med Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare

100KG
MOQ
*USD
Price
Sabic Lexan HP6NR Resin Is Low/Med Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 7
UL Recognized, 94V-2 Flame Class Rating (3): 1.47
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: HP6NR
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  HP6NR resin is Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible(ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no mold release.

 


Property

MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 68 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 135 % ASTM D 638
Tensile Modulus, 5 mm/min 2310 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 97 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790
Hardness, Rockwell M 70 - ASTM D 785
Hardness, Rockwell R 118 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044
Tensile Stress, yield, 50 mm/min 60 MPa ISO 527
Tensile Stress, break, 50 mm/min 75 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 140 % ISO 527
Tensile Modulus, 1 mm/min 2300 MPa ISO 527
Flexural Stress, yield, 2 mm/min 95 MPa ISO 178
Flexural Modulus, 2 mm/min 2250 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 3204 J/m ASTM D 4812
Izod Impact, notched, 23°C 907 J/m ASTM D 256
Izod Impact, notched, -30°C 139 J/m ASTM D 256
Tensile Impact, Type "S" 630 kJ/m² ASTM D 1822
Falling Dart Impact (D 3029), 23°C 169 J ASTM D 3029
Instrumented Impact Energy @ peak, 23°C 64 J ASTM D 3763
Instrumented Impact Total Energy, 23°C 65 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 75 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 15 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 75 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 15 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 135 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 124 °C ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.2E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 5.7E-05 1/°C ASTM E 831
CTE, -40°C to 95°C, flow 6.84E-05 1/°C ASTM E 831
Specific Heat 1.25 J/g-°C ASTM C 351
Thermal Conductivity 0.19 W/m-°C ASTM C 177
CTE, -40°C to 40°C, flow 6.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 6.E-05 1/°C ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 143 °C ISO 306
Vicat Softening Temp, Rate B/120 140 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 124 °C ISO 75/Af
Relative Temp Index, Elec 130 °C UL 746B
Relative Temp Index, Mech w/impact 130 °C UL 746B
Relative Temp Index, Mech w/o impact 130 °C UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Specific Volume 0.83 cm³/g ASTM D 792
Density 1.19 g/cm³ ASTM D 792
Water Absorption, 24 hours 0.15 % ASTM D 570
Water Absorption, equilibrium, 23C 0.35 % ASTM D 570
Water Absorption, equilibrium, 100°C 0.58 % ASTM D 570
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % SABIC Method
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Mold Shrinkage, xflow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 7 g/10 min ASTM D 1238
Melt Flow Rate, 300°C/5.0 kgf 112.2 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 7 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze 1 % ASTM D 1003
Refractive Index 1.586 - ASTM D 542
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+17 Ohm-cm ASTM D 257
Dielectric Strength, in air, 3.2 mm 14.9 kV/mm ASTM D 149
Relative Permittivity, 50/60 Hz 3.17 - ASTM D 150
Relative Permittivity, 1 MHz 2.96 - ASTM D 150
Dissipation Factor, 50/60 Hz 0.0009 - ASTM D 150
Dissipation Factor, 1 MHz 0.01 - ASTM D 150
Hot Wire Ignition {PLC) 2 PLC Code UL 746A
High Voltage Arc Track Rate {PLC} 2 PLC Code UL 746A
High Ampere Arc Ign, surface {PLC} 1 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC} 2 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94HB Flame Class Rating (3) 1.47 mm UL 94
Source GMD, last updated:11/22/2006    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 310 - 330 °C
Nozzle Temperature 305 - 325 °C
Front - Zone 3 Temperature 310 - 330 °C
Middle - Zone 2 Temperature 300 - 320 °C
Rear - Zone 1 Temperature 290 - 310 °C
Mold Temperature 80 - 115 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:11/22/2006  

 

 


 

For more information please download the datasheet

Sabic Lexan HP6NR Resin Is Low/Med Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare 0  Sabic Lexan HP6NR.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan HP6NR Resin Is Low/Med Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)