Sabic Lexan LR200G3 Is A 30 % Glass Fibre Reinforced Material Used For Non-Cosmetic Injection Moulding Applications.

100KG
MOQ
*USD
Price
Sabic Lexan LR200G3 Is A 30 % Glass Fibre Reinforced Material Used For Non-Cosmetic Injection Moulding Applications.
Features Gallery Product Description Request A Quote
Features
Specifications
UL Recognized, 94V-0 Flame Class Rating (3: 1.7
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: LR200G3
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  LR200G3 resin is a 30 % glass fibre reinforced material used for non-cosmetic injection moulding applications.


 

Property

 

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, break, 5 mm/min 90 MPa ISO 527
Tensile Strain, break, 5 mm/min 2 % ISO 527
Tensile Modulus, 1 mm/min 7500 MPa ISO 527
Flexural Stress, break, 2 mm/min 115 MPa ISO 178
Flexural Modulus, 2 mm/min 6000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched 80*10*4 +23°C 25 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 5 kJ/m² ISO 180/1A
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm 30 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
CTE, 23°C to 80°C, flow 2.5E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.5E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 147 °C ISO 306
Vicat Softening Temp, Rate B/120 145 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 140 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 135 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Mold Shrinkage on Tensile Bar, flow (2) (5) 0.1 - 0.4 % SABIC Method
Density 1.44 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.3 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.12 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 5 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 3.2 mm 16 kV/mm IEC 60243-1
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3) 1.7 mm UL 94
Source GMD, last updated:2002/05/22    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 290 - 320 °C
Nozzle Temperature 280 - 310 °C
Front - Zone 3 Temperature 290 - 320 °C
Middle - Zone 2 Temperature 280 - 310 °C
Rear - Zone 1 Temperature 270 - 300 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 80 - 120 °C
Source GMD, last updated:2002/05/22  

 

For more information please download the datasheet

Sabic Lexan LR200G3 Is A 30 % Glass Fibre Reinforced Material Used For Non-Cosmetic Injection Moulding Applications. 0  Sabic Lexan LR200G3.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan LR200G3 Is A 30 % Glass Fibre Reinforced Material Used For Non-Cosmetic Injection Moulding Applications. 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)