Sabic Lexan EXL1413T Polycarbonate (PC) Siloxane Copolymer Resin Is A Transparent Injection Molding Grade

100KG
MOQ
*USD
Price
Sabic Lexan EXL1413T Polycarbonate (PC) Siloxane Copolymer Resin Is A Transparent Injection Molding Grade
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 10
UL Recognized, 94V-2 Flame Class Rating (3): 2.5
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: EXL1413T
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  EXL1413T resin is polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. Lexan EXL1413T resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 58 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 64 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5.8 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 131.4 % ASTM D 638
Tensile Modulus, 50 mm/min 2210 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 94 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2210 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 57 MPa ISO 527
Tensile Stress, break, 50 mm/min 61 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5.5 % ISO 527
Tensile Strain, break, 50 mm/min 124.9 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2150 MPa ISO 178
Hardness, Rockwell L 89 - ISO 2039-2
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 890 J/m ASTM D 256
Izod Impact, notched, -30°C 795 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 82 J ASTM D 3763
Instrumented Impact Total Energy, -30°C 85 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 55 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 60 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate A/50 141 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 124 °C ASTM D 648
CTE, -40°C to 95°C, flow 7.15E-05 1/°C ASTM E 831
CTE, -40°C to 95°C, xflow 7.93E-05 1/°C ASTM E 831
CTE, 23°C to 80°C, flow 7.15E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.93E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C pass - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 141 °C ISO 306
Vicat Softening Temp, Rate B/120 142 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 118 °C ISO 75/Af
Relative Temp Index, Elec 130 °C UL 746B
Relative Temp Index, Mech w/o impact 130 °C UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.4 - 0.8 % SABIC Method
Mold Shrinkage, xflow, 3.2 mm 0.4 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 10 g/10 min ASTM D 1238
Density 1.19 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.12 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.09 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 9 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 82 % ASTM D 1003
Haze 3 % ASTM D 1003
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm ASTM D 257
Surface Resistivity >1.E+15 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-2 Flame Class Rating (3) 2.5 mm UL 94
Glow Wire Flammability Index 960°C, passes at 3 mm IEC 60695-2-12
Glow Wire Ignitability Temperature, 0.8 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm 825 °C IEC 60695-2-13
Source GMD, last updated:09/15/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 215 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:09/15/2004  

 

For more information please download the datasheet

Sabic Lexan EXL1413T Polycarbonate (PC) Siloxane Copolymer Resin Is A Transparent Injection Molding Grade 0  Sabic Lexan EXL1413T.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan EXL1413T Polycarbonate (PC) Siloxane Copolymer Resin Is A Transparent Injection Molding Grade 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)