Send Message

Sabic Lexan EXL1182C High Flow, UV Stabilized, Polycarbonate Siloxane Copolymer Resin. Notched Izod Ductile To -20C D

100KG
MOQ
*USD
Price
Sabic Lexan EXL1182C High Flow, UV Stabilized, Polycarbonate Siloxane Copolymer Resin. Notched Izod Ductile To -20C D
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 20
UL Recognized, 94V-2 Flame Class Rating (3): 1.5
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: EXL1182C
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  EXL1182C resin is High flow, UV stabilized, polycarbonate siloxane copolymer resin. Notched izod ductile to -20C ductility. Enhanced processability compared to standard PC resins. Available in a range of transparent colors.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 59 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 59 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5.4 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 125.1 % ASTM D 638
Tensile Modulus, 5 mm/min 2350 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 96 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2300 MPa ASTM D 790
Hardness, Rockwell L 92 - ASTM D 785
Tensile Stress, yield, 50 mm/min 59 MPa ISO 527
Tensile Stress, break, 50 mm/min 59 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5.3 % ISO 527
Tensile Strain, break, 50 mm/min 122.5 % ISO 527
Tensile Modulus, 1 mm/min 2460 MPa ISO 527
Flexural Stress, yield, 2 mm/min 91 MPa ISO 178
Flexural Modulus, 2 mm/min 2220 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 737 J/m ASTM D 256
Izod Impact, notched, -10°C 616 J/m ASTM D 256
Izod Impact, notched, -20°C 577 J/m ASTM D 256
Izod Impact, notched, -30°C 426 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 70 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 60 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 20 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 60 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 20 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate A/50 137 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 119 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.15E-04 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 6.45E-04 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 6.15E-04 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 6.45E-04 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 137 °C ISO 306
Vicat Softening Temp, Rate B/120 139 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 116 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.18 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.4 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 20 g/10 min ASTM D 1238
Density 1.18 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.29 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.1 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 19 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 86 % ASTM D 1003
Haze 1.4 % ASTM D 1003
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94HB Flame Class Rating (3) 1.5 mm UL 94
UL Recognized, 94V-2 Flame Class Rating (3) 2.5 mm UL 94
Source GMD, last updated:04/09/2007    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 270 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:04/09/2007  

 

For more information please download the datasheet

Sabic Lexan EXL1182C High Flow, UV Stabilized, Polycarbonate Siloxane Copolymer Resin. Notched Izod Ductile To -20C D 0  Sabic Lexan EXL1182C.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan EXL1182C High Flow, UV Stabilized, Polycarbonate Siloxane Copolymer Resin. Notched Izod Ductile To -20C D 1Click to consult and get the latest quotation within 24 hours!

 