Sabic Lexan HP2EU Resin Is Med/High Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare

100KG
MOQ
*USD
Price
Sabic Lexan HP2EU Resin Is Med/High Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 22
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: HP2EU
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  HP2EU resin is Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible(ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold release.

 


Property

MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 630 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 700 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 125 % ASTM D 638
Tensile Modulus, 5 mm/min 630 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 980 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2350 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 65 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 100 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 70 J/m ASTM D 256
Izod Impact, notched, -30°C 30 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 633 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 60 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 10 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 65 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 10 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy Impact, notched, 23°C 35 kJ/m² ISO 179/2C
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 139 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 129 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.8E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 6.8E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 7.E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 140 °C ISO 306
Vicat Softening Temp, Rate B/120 141 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 133 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 122 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % SABIC Method
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 22 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 21 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze <0.8 % ASTM D 1003
Source GMD, last updated:03/15/2007    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 280 - 300 °C
Nozzle Temperature 270 - 290 °C
Front - Zone 3 Temperature 280 - 300 °C
Middle - Zone 2 Temperature 270 - 290 °C
Rear - Zone 1 Temperature 260 - 280 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 80 - 100 °C
Source GMD, last updated:03/15/2007  

 

 


 

For more information please download the datasheet

Sabic Lexan HP2EU Resin Is Med/High Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare 0  Sabic Lexan HP2EU.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan HP2EU Resin Is Med/High Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)