Sabic Lexan LGK5030 Glass Reinforced. Flame Retardant.

100KG
MOQ
*USD
Price
Sabic Lexan LGK5030 Glass Reinforced. Flame Retardant.
Features Gallery Product Description Request A Quote
Features
Specifications
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: LGK5030
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  LGK5030 resin is Glass reinforced. Flame retardant.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, brk, Type I, 50 mm/min 142 MPa ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 4 % ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span 186 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 10700 MPa ASTM D 790
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 122 J/m ASTM D 256
THERMAL Value Unit Standard
HDT, 1.82 MPa, 6.4 mm, unannealed 143 °C ASTM D 648
CTE, -30°C to 30°C, flow 2.16E-05 1/°C ASTM D 696
CTE, -30°C to 30°C, xflow 3.96E-05 1/°C ASTM D 696
PHYSICAL Value Unit Standard
Specific Gravity 1.61 - ASTM D 792
Water Absorption, 24 hours 0.14 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm 0.05 - 0.25 % SABIC Method
Mold Shrinkage, xflow, 3.2 mm 0.1 - 0.3 % SABIC Method
ELECTRICAL Value Unit Standard
Dielectric Strength, in oil, 3.2 mm 16.3 kV/mm ASTM D 149
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-1 Flame Class Rating (3) 1.47 mm UL 94
UL Recognized, 94V-0 Flame Class Rating (3) 2.79 mm UL 94
UL Recognized, 94-5VA Rating (3) 3.6 mm UL 94
Source GMD, last updated:01/04/2000    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 315 - 340 °C
Nozzle Temperature 310 - 330 °C
Front - Zone 3 Temperature 315 - 340 °C
Middle - Zone 2 Temperature 305 - 325 °C
Rear - Zone 1 Temperature 295 - 315 °C
Mold Temperature 80 - 115 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:01/04/2000  

 

 


 

For more information please download the datasheet

Sabic Lexan LGK5030 Glass Reinforced. Flame Retardant. 0  Sabic Lexan LGK5030.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan LGK5030 Glass Reinforced. Flame Retardant. 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)