Sabic Lexan HFR1720 Resin Is 25 MFR PC Resin. Good Clarity, Heat Resistance, Property Retention And Dimensional Stabilit

100KG
MOQ
*USD
Price
Sabic Lexan HFR1720 Resin Is 25 MFR PC Resin. Good Clarity, Heat Resistance, Property Retention And Dimensional Stabilit
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 25
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: HFR1720
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan HFR1720 resin is 25 MFR PC resin. Good clarity, heat resistance, property retention and dimensional stability.

 


Property

MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 65 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 120 % ASTM D 638
Tensile Modulus, 50 mm/min 2380 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 93 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2300 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 50 MPa ISO 527
Tensile Strain, yield, 50 mm/min 60 % ISO 527
Tensile Strain, break, 50 mm/min 70 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 640 J/m ASTM D 256
Izod Impact, notched 80*10*4 +23°C 12 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT, 1.82 MPa, 3.2mm, unannealed 126 °C ASTM D 648
Vicat Softening Temp, Rate B/120 140 °C ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 121 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 25 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 26 cm³/10 min ISO 1133
Source GMD, last updated:03/02/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 270 - 295 °C
Nozzle Temperature 265 - 290 °C
Front - Zone 3 Temperature 270 - 295 °C
Middle - Zone 2 Temperature 260 - 280 °C
Rear - Zone 1 Temperature 250 - 270 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:03/02/2004  

 

 


 

For more information please download the datasheet

Sabic Lexan HFR1720 Resin Is 25 MFR PC Resin. Good Clarity, Heat Resistance, Property Retention And Dimensional Stabilit 0  Sabic Lexan HFR1720.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan HFR1720 Resin Is 25 MFR PC Resin. Good Clarity, Heat Resistance, Property Retention And Dimensional Stabilit 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)