Sabic Lexan EXL1036 Polycarbonate (PC) Siloxane Copolymer Resin Is A UV Stabilized High Viscosity Grade

100KG
MOQ
*USD
Price
Sabic Lexan EXL1036 Polycarbonate (PC) Siloxane Copolymer Resin Is A UV Stabilized High Viscosity Grade
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 300°C/1.2 Kg: 5
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: EXL1036
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  EXL1036 resin is polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good hiding power as caplayer in combination with excellent extrusion processing characteristics. Lexan EXL1036 resin is available in limited opaque colors only and is an excellent candidate for a broad range of (co-)extrusion/thermoforming applications.
 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 58 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 65 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 130 % ASTM D 638
Tensile Modulus, 50 mm/min 2120 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 88 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2100 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 57 MPa ISO 527
Tensile Stress, break, 50 mm/min 66 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 120 % ISO 527
Tensile Modulus, 1 mm/min 2070 MPa ISO 527
Flexural Stress, yield, 2 mm/min 80 MPa ISO 178
Flexural Modulus, 2 mm/min 1960 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 820 J/m ASTM D 256
Izod Impact, notched, -30°C 680 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 52 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 55 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 75 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 60 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 143 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 121 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.66E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 6.66E-05 1/°C ASTM E 831
CTE, 23°C to 80°C, flow 7.2E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.2E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 143 °C ISO 306
Vicat Softening Temp, Rate B/120 141 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 125 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.4 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 5.5 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 5 cm³/10 min ISO 1133
Source GMD, last updated:11/08/2006    

Processing

Parameter    
Sheet Extrusion Value Unit
Drying Temperature 110 - 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 245 - 260 °C
Barrel - Zone 1 Temperature 250 - 290 °C
Barrel - Zone 2 Temperature 245 - 270 °C
Barrel - Zone 3 Temperature 225 - 255 °C
Adapter Temperature 225 - 255 °C
Die Temperature 240 - 260 °C
Roll Stack Temp - Top 75 - 115 °C
Roll Stack Temp - Middle 80 - 125 °C
Roll Stack Temp - Bottom 120 - 145 °C
Source GMD, last updated:11/08/2006  

 
 


 

For more information please download the datasheet

Sabic Lexan EXL1036 Polycarbonate (PC) Siloxane Copolymer Resin Is A UV Stabilized High Viscosity Grade 0  Sabic Lexan EXL1036.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan EXL1036 Polycarbonate (PC) Siloxane Copolymer Resin Is A UV Stabilized High Viscosity Grade 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)