Sabic Lexan HFD1413 Resin Is 11 MFR High Flow Ductile Copolymer

100KG
MOQ
*USD
Price
Sabic Lexan HFD1413 Resin Is 11 MFR High Flow Ductile Copolymer
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 11
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: HFD1413
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  HFD1413 resin is 11 MFR High Flow Ductile Copolymer

 


Property

MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 58 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 67 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 137 % ASTM D 638
Tensile Modulus, 5 mm/min 2240 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 98 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2230 MPa ASTM D 790
Hardness, Rockwell R 120 - ASTM D 785
Tensile Stress, yield, 50 mm/min 61 MPa ISO 527
Tensile Stress, break, 50 mm/min 68 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 126 % ISO 527
Tensile Modulus, 1 mm/min 2120 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2090 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 903 J/m ASTM D 256
Izod Impact, notched, -20°C 859 J/m ASTM D 256
Izod Impact, notched, -30°C 435 J/m ASTM D 256
Multiaxial Impact 120 J ISO 6603
Instrumented Impact Total Energy, 23°C 77 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 32 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 80 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 43 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 136 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 124 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 114 °C ASTM D 648
CTE, -40°C to 40°C, flow 8.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 8.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 8.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 8.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASS - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 130 °C ISO 306
Vicat Softening Temp, Rate B/120 131 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 115 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Density 1.2 g/cm³ ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5) 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 11 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.3 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 10 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission, 2.54 mm 88 % ASTM D 1003
Haze, 2.54 mm <1 % ASTM D 1003
Refractive Index 1.582 - ASTM D 542
Source GMD, last updated:2010/02/28    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 270 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:2010/02/28  

 

 


 

For more information please download the datasheet

Sabic Lexan HFD1413 Resin Is 11 MFR High Flow Ductile Copolymer 0  Sabic Lexan HFD1413.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan HFD1413 Resin Is 11 MFR High Flow Ductile Copolymer 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)