S-Plastics Lexan DMX6014 resin is an injection moldable PC copolymer ABS blend. This resin combines excellent scratch resistance (F-pencil hardness) with
ductility.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 53 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 45 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 45 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 75 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2200 | MPa | ASTM D 790 |
| Hardness, Rockwell L | 90 | - | ASTM D 785 |
| Hardness, Rockwell R | 117 | - | ASTM D 785 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 48 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2150 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2150 | MPa | ISO 178 |
| Pencil Hardness test, 1kgf | F | - | ASTM D 3363 |
| Erichson scratch depth, 6N | 14 | micrometer | S-Plastics Method |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 220 | J/m | ASTM D 256 |
| Multiaxial Impact | 55 | J | ISO 6603 |
| Izod Impact, notched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 97 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/120 | 118 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.15 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 12 | g/10 min | ASTM D 1238 |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:03/06/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 100 - 110 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 290 | °C |
| Nozzle Temperature | 240 - 280 | °C |
| Front - Zone 3 Temperature | 250 - 290 | °C |
| Middle - Zone 2 Temperature | 250 - 290 | °C |
| Rear - Zone 1 Temperature | 230 - 260 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 90 | °C |
| Source GMD, last updated:03/06/2008 | ||
For more information please download the datasheet | |
 | S-Plastics Lexan DMX6014.pdf |