Sabic Lexan ML3041 has been developed for the injection moulding of thin-wall complex parts that require high mechanica

100KG
MOQ
*USD
Price
Sabic Lexan ML3041 has been developed for the injection moulding of thin-wall complex parts that require high mechanica
Features Gallery Product Description Request A Quote
Features
Specifications
UL Recognized, 94HB Flame Class Rating (3): 1
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: ML3041
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  ML3041 resin is  has been developed for the injection moulding of thin-wall, complex parts that require high mechanical properties and impact resistance.


Property

MECHANICAL Value Unit Standard
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy SABIC Method
Tensile Stress, yield, 50 mm/min 60 MPa ISO 527
Tensile Stress, break, 50 mm/min 63 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 105 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 88 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
Hardness, H358/30 85 MPa ISO 2039-1
IMPACT Value Unit Standard
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 14 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 65 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 17 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy Impact, notched, 23°C 40 kJ/m² ISO 179/2C
Charpy Impact, notched, -20°C 20 kJ/m² ISO 179/2C
THERMAL Value Unit Standard
Thermal Conductivity 0.2 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 143 °C ISO 306
Vicat Softening Temp, Rate B/120 141 °C ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 121 °C ISO 75/Ae
Relative Temp Index, Elec 80 °C UL 746B
Relative Temp Index, Mech w/impact 80 °C UL 746B
Relative Temp Index, Mech w/o impact 80 °C UL 746B
PHYSICAL Value Unit Standard
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % SABIC Method
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 10 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Haze NA % ASTM D 1003
Refractive Index NA - ISO 489
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 0.8 mm 35 kV/mm IEC 60243-1
Dielectric Strength, in oil, 1.6 mm 27 kV/mm IEC 60243-1
Dielectric Strength, in oil, 3.2 mm 17 kV/mm IEC 60243-1
Relative Permittivity, 50/60 Hz 2.7 - IEC 60250
Relative Permittivity, 1 MHz 2.7 - IEC 60250
Dissipation Factor, 50/60 Hz 0.001 - IEC 60250
Dissipation Factor, 1 MHz 0.01 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-2 Flame Class Rating (3) 1 mm UL 94
Glow Wire Flammability Index 850°C, passes at 1 mm IEC 60695-2-12
Oxygen Index (LOI) 25 % ISO 4589
Source GMD, last updated:07/31/1997    

Processing

Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 280 - 300 °C
Nozzle Temperature 270 - 290 °C
Front - Zone 3 Temperature 280 - 300 °C
Middle - Zone 2 Temperature 270 - 290 °C
Rear - Zone 1 Temperature 260 - 280 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 80 - 100 °C
Source GMD, last updated:07/31/1997  
     
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.    
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION    
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
   
(2) Only typical data for selection purposes. Not to be used for part or tool design.    
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.    
(4) Internal measurements according to UL standards.    

 

For more information please download the datasheet

Sabic Lexan ML3041 has been developed for the injection moulding of thin-wall complex parts that require high mechanica 0  Sabic Lexan ML3041.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan ML3041 has been developed for the injection moulding of thin-wall complex parts that require high mechanica 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)