S-Plastics Lexan FXM941A resin is PC in special effects colors. Metallic and pearlescent additives. Color package may affect performance.
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min | 61 | MPa | ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min | 57 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min | 95 | % | ASTM D 638 |
Tensile Modulus, 50 mm/min | 2300 | MPa | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 95 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2390 | MPa | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched, 23°C | 160 | J/m | ASTM D 256 |
Instrumented Impact Total Energy, 23°C | 59 | J | ASTM D 3763 |
THERMAL | Value | Unit | Standard |
HDT, 0.45 MPa, 3.2 mm, unannealed | 137 | °C | ASTM D 648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 126 | °C | ASTM D 648 |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.2 | - | ASTM D 792 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
Melt Flow Rate, 300°C/1.2 kgf | 10.2 | g/10 min | ASTM D 1238 |
ELECTRICAL | Value | Unit | Standard |
Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D 495 |
Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A |
High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A |
High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A |
Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized, 94V-2 Flame Class Rating (3) | 1.52 | mm | UL 94 |
UL Recognized, 94V-0 Flame Class Rating (3) | 3.04 | mm | UL 94 |
Source GMD, last updated:08/16/2000 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 3 - 4 | hrs |
Drying Time (Cumulative) | 48 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 295 - 315 | °C |
Nozzle Temperature | 290 - 310 | °C |
Front - Zone 3 Temperature | 295 - 315 | °C |
Middle - Zone 2 Temperature | 280 - 305 | °C |
Rear - Zone 1 Temperature | 270 - 295 | °C |
Mold Temperature | 70 - 95 | °C |
Back Pressure | 0.3 - 0.7 | MPa |
Screw Speed | 40 - 70 | rpm |
Shot to Cylinder Size | 40 - 60 | % |
Vent Depth | 0.025 - 0.076 | mm |
Source GMD, last updated:08/16/2000 |
For more information please download the datasheet |
|
![]() |
S-Plastics Lexan FXM941A.pdf |
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
|