S-Plastics Lexan FXM4701 resin is FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 66 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 78 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | >50 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2250 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 97 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2350 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 64 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, -30°C | NB | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 300 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 54 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 149 | °C | ASTM D 648 |
| CTE, -40°C to 95°C, flow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 95°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C to 80°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 175 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 170 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 165 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 150 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.8 - 1 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.8 - 1 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 2 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 6 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 330°C/2.16kg | 8 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:10/07/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 125 - 135 | °C |
| Drying Time | 3 - 4 | hrs |
| Melt Temperature | 325 - 360 | °C |
| Nozzle Temperature | 320 - 340 | °C |
| Front - Zone 3 Temperature | 320 - 340 | °C |
| Middle - Zone 2 Temperature | 310 - 330 | °C |
| Rear - Zone 1 Temperature | 300 - 320 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 100 - 125 | °C |
| Source GMD, last updated:10/07/2004 | ||
|
For more information please download the datasheet |
|
 |