S-Plastics Lexan FXM2034 resin isLEXAN FXM2034 is a medium viscosity metallic VisualFX grade designed to pass GWI 850C at 3mm thickness
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yield, 50 mm/min | 71 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 10 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2650 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 79 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2600 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched 80*10*3 +23°C | 7 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 7 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 128 | °C | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Density | 1.24 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm³/10 min | ISO 1133 |
Source GMD, last updated:02/28/2008 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 2 - 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 280 - 310 | °C |
Nozzle Temperature | 270 - 290 | °C |
Front - Zone 3 Temperature | 280 - 310 | °C |
Middle - Zone 2 Temperature | 270 - 290 | °C |
Rear - Zone 1 Temperature | 260 - 280 | °C |
Hopper Temperature | 60 - 80 | °C |
Mold Temperature | 80 - 110 | °C |
Source GMD, last updated:02/28/2008 |