Sabic Lexan ML7647 Non FR Impact Modified PC Excellent Fatigue Performance With Balanced Flow And Impact In Opaque Only

100KG
MOQ
*USD
Price
Sabic Lexan ML7647 Non FR Impact Modified PC Excellent Fatigue Performance With Balanced Flow And Impact  In Opaque Only
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 10.7
UL Recognized, 94HB Flame Class Rating (3): ???
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: ML7647
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  ML7647 resin is Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque only


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 52 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 54 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5.3 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 110 % ASTM D 638
Tensile Modulus, 50 mm/min 2180 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 87 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2130 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 53 MPa ISO 527
Tensile Stress, break, 50 mm/min 50 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5.7 % ISO 527
Tensile Strain, break, 50 mm/min 94 % ISO 527
Tensile Modulus, 1 mm/min 2150 MPa ISO 527
Flexural Stress, yield, 2 mm/min 84 MPa ISO 178
Flexural Modulus, 2 mm/min 2220 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 770 J/m ASTM D 256
Izod Impact, notched, -30°C 720 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 69 J ASTM D 3763
Izod Impact, notched 80*10*4 +23°C 57 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C 49 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 60 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 138 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 120 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.94E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 7.2E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 7.09E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 7.48E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 138 °C ISO 306
Vicat Softening Temp, Rate B/120 140 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 119 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 10.7 g/10 min ASTM D 1238
Density 1.19 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.26 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 10 cm³/10 min ISO 1133
Source GMD, last updated:01/23/2006    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 270 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:01/23/2006  
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.    
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION  
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.    
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.  
(4) Internal measurements according to UL standards.    

 


 

For more information please download the datasheet

Sabic Lexan ML7647 Non FR Impact Modified PC Excellent Fatigue Performance With Balanced Flow And Impact  In Opaque Only 0  Sabic Lexan ML7647.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan ML7647 Non FR Impact Modified PC Excellent Fatigue Performance With Balanced Flow And Impact  In Opaque Only 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)