S-Plastic Lexan"FXM141R Is A Lexan PC Grade In Metallic Or Pearlescent Effect, Which Is Part Of The VisualFX Family.

100KG
MOQ
*USD
Price
S-Plastic Lexan"FXM141R Is A Lexan PC Grade In Metallic Or Pearlescent Effect, Which Is Part Of The VisualFX Family.
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 10.8
UL Recognized, 94HB Flame Class Rating (3): 0.7
Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: FXM141R
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Lexan FXM141R resin is FXM141R is a Lexan PC grade in Metallic or Pearlescent effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect properties, Application testing always reccomended.


Property

MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 55 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6.2 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 90 % ASTM D 638
Tensile Modulus, 5 mm/min 2340 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 94 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 55 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 50 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
Hardness, H358/30 95 MPa ISO 2039-1
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C NB J/m ASTM D 4812
Izod Impact, notched, 23°C 214 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 54 J ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 10 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C 8 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 12 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm 13 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 138 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 127 °C ASTM D 648
CTE, -40°C to 95°C, flow 6.87E-05 1/°C ASTM E 831
CTE, -40°C to 95°C, xflow 6.95E-05 1/°C ASTM E 831
CTE, 23°C to 80°C, flow 6.96E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.06E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 141 °C ISO 306
Vicat Softening Temp, Rate B/120 142 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 136 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 125 °C ISO 75/Ae
Relative Temp Index, Elec 80 °C UL 746B
Relative Temp Index, Mech w/impact 80 °C UL 746B
Relative Temp Index, Mech w/o impact 80 °C UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % S-Plastics Method
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 300°C/1.2 kgf 10.8 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 11 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Hot Wire Ignition {PLC) 2 PLC Code UL 746A
High Voltage Arc Track Rate {PLC} 2 PLC Code UL 746A
High Ampere Arc Ign, surface {PLC} 1 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC} 3 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94HB Flame Class Rating (3) 0.7 mm UL 94
UV-light, water exposure/immersion F2 - UL 746C
Source GMD, last updated:10/24/2003    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 270 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:10/24/2003  

 

For more information please download the datasheet

S-Plastic Lexan"FXM141R Is A Lexan PC Grade In Metallic Or Pearlescent Effect, Which Is Part Of The VisualFX Family. 0  S-Plastics Lexan"FXM141R.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic Lexan"FXM141R Is A Lexan PC Grade In Metallic Or Pearlescent Effect, Which Is Part Of The VisualFX Family. 1Click to consult and get the latest quotation within 24 hours!

 

S-Plastics lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)