Sabic Lexan 945ASR Polycarbonate (PC) Resin Non-Filled, Injection Moldable Grade. This Non-Chlorinated, Non-Brominat

100KG
MOQ
*USD
Price
Sabic Lexan 945ASR Polycarbonate (PC) Resin Non-Filled, Injection Moldable Grade. This Non-Chlorinated, Non-Brominat
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 10
UL Recognized, 94V-2 Flame Class Rating (3): 1.5
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: 945ASR
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  945ASR resin is Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 68 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 125 % ASTM D 638
Tensile Modulus, 50 mm/min 2280 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 101 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2380 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 65 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 100 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 801 J/m ASTM D 256
Izod Impact, notched, -30°C 128 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 79 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 12 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 73 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 14 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 143 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 138 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 127 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.84E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 7.38E-05 1/°C ASTM E 831
Thermal Conductivity 0.2 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 141 °C ISO 306
Vicat Softening Temp, Rate B/120 142 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 136 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 125 °C ISO 75/Ae
Relative Temp Index, Elec 130 °C UL 746B
Relative Temp Index, Mech w/impact 120 °C UL 746B
Relative Temp Index, Mech w/o impact 130 °C UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % SABIC Method
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 10 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 10 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission >88 % ASTM D 1003
Haze <2 % ASTM D 1003
ELECTRICAL Value Unit Standard
Arc Resistance, Tungsten {PLC} 7 PLC Code ASTM D 495
Hot Wire Ignition {PLC) 3 PLC Code UL 746A
High Voltage Arc Track Rate {PLC} 3 PLC Code UL 746A
High Ampere Arc Ign, surface {PLC} 3 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC} 2 PLC Code UL 746A
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 3.2 mm 17 kV/mm IEC 60243-1
Relative Permittivity, 50/60 Hz 2.7 - IEC 60250
Relative Permittivity, 1 MHz 2.7 - IEC 60250
Dissipation Factor, 50/60 Hz 0.001 - IEC 60250
Dissipation Factor, 1 MHz 0.01 - IEC 60250
Comparative Tracking Index 225 V IEC 60112
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-2 Flame Class Rating (3) 1.5 mm UL 94
UL Recognized, 94V-0 Flame Class Rating (3) 3 mm UL 94
Glow Wire Flammability Index 960°C, passes at 1 mm IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm 850 °C IEC 60695-2-13
Oxygen Index (LOI) 35 % ISO 4589
Source GMD, last updated:10/21/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 280 - 310 °C
Nozzle Temperature 270 - 290 °C
Front - Zone 3 Temperature 280 - 310 °C
Middle - Zone 2 Temperature 270 - 290 °C
Rear - Zone 1 Temperature 260 - 280 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 80 - 110 °C
Source GMD, last updated:10/21/2004  

 


 

For more information please download the datasheet

Sabic Lexan 945ASR Polycarbonate (PC) Resin Non-Filled, Injection Moldable Grade. This Non-Chlorinated, Non-Brominat 0  Sabic Lexan 945ASR.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan 945ASR Polycarbonate (PC) Resin Non-Filled, Injection Moldable Grade. This Non-Chlorinated, Non-Brominat 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)